Resumen
The dramatic increase in sewage sludge production requires researchers to develop and explore more commercially viable ways for alleviating current environmental and socioeconomic challenges connected with its routine management. It has been established that sewage sludge can be processed to fabricate various valuable products or as fuels for electricity generation. In this research, kaolin (calcined from coal gangue) and sewage sludge were successfully used to prepare porous ceramic bricks without any additives. The effect of sewage sludge on the microstructure, phase composition, and mechanical properties of kaolin-sewage sludge ceramic bricks was investigated. The results show that the kaolin-sewage sludge ceramic bricks are mainly composed of mullite (3Al2O3·2SiO2), sillimanite (Al2SiO5), aluminum phosphate (AlPO4), hematite (Fe2O3) as well as a small amount of quartz (SiO2). The ceramic bricks present a typical porous structure, and the number and size of micropores increases noticeably with the increase of sewage sludge content. The sintering shrinkage rate and porosity of ceramic bricks increased significantly with the increase of sewage sludge content, which is mainly attributed to the increase of liquid phase proportion and high temperature volatilization. Sewage sludge can significantly improve the mechanical properties of kaolin-sewage sludge ceramic bricks. When the sewage sludge content is 30 wt.%, the ceramic bricks present the maximum compressive strength and flexural strength and high porosity (32.74%). The maximum sintering shrinkage rate and porosity are 12.17% and 40.51%, respectively.