Microstructure and Tribological Performance of TiB2-NiCr Composite Coating Deposited by APS

Ning Zhang    
Nannan Zhang    
Xufeng Wei    
Yue Zhang and Deyuan Li    

Resumen

Nickel chromium (NiCr) powders with different titanium diboride (TiB2) additions (20, 40 and 60 wt %) were prepared with a mechanical alloying method and then sprayed using an air plasma spraying technology. The microstructure and phase composite of the powders and the cross-sections of deposited coatings were analyzed with a scanning electronic microscope and X-ray diffraction. The tribological performance of the coatings was studied using a pin-on-disk tribometer at room temperature. The weight loss of the as-sprayed coating was measured by using a high accuracy weighing balance. Cr3C2-25NiCr coating was produced and tested for comparison. The morphologies of the worn surface were then investigated. Parts of debris with some scratches were found, presenting typical signs of abrasive wear and showing slight adhesive wear on the surface. The 20 wt % additive TiB2 coating demonstrated the highest microhardness and the lowest coefficient of friction. The wear resistance of the metal-ceramic composites coatings was enhanced with the addition of TiB2.

 Artículos similares

       
 
Jianjun Hu, Chuan He, Xian Yang, Hui Li, Hongbin Xu and Ning Guo    
The FeS solid lubricating coatings were prepared on the AISI 5140 steel by chemical bath deposition (CBD) coating technique at various temperatures from 30 to 90 °C. The influence of temperature on microstructure, microcracks, and tribological properties... ver más
Revista: Applied Sciences

 
Lixia Ying, Zhen Fu, Ke Wu, Chunxi Wu, Tengfei Zhu, Yue Xie and Guixiang Wang    
The aim of this paper is to obtain Cu–Sn composite coatings incorporated with PTFE and TiO2 particles, which have superior antiwear and friction reduction properties. Electrodeposition was carried out in a pyrophosphate electrolyte, and the electro... ver más
Revista: Coatings

 
Haijuan Mei, Rui Wang, Xing Zhong, Wei Dai and Qimin Wang    
In this study, Mo-Cu-V-N composite coatings with high Cu content of ~18 at.% were deposited on 316L stainless steel and YT14 cemented carbide substrates by high power impulse magnetron sputtering in Ar?N2 gas mixtures. The influence of N2 partial pressur... ver más
Revista: Coatings

 
Ming Cao, Lan Zhao, Libin Wu and Wenquan Wang    
The increasing demands of environmental protection have led to solid lubricant coatings becoming more and more important. A new type of MoS2-based coating co-doped with Cu and Al prepared by magnetron sputtering, including Cu/MoS2 and Cu-Al/MoS2 coatings... ver más
Revista: Coatings

 
Zhaoxiang Chen, Xipeng Ren, Limei Ren, Tengchao Wang, Xiaowen Qi and Yulin Yang    
Spark-anodization of titanium can produce adherent and wear-resistant TiO2 film on the surface, but the spark-anodized titanium has lots of surface micro-pores, resulting in an unstable and high friction coefficient against many counterparts. In this stu... ver más
Revista: Coatings