Hamza Alkuime, Emad Kassem, Khaled A. Alshraiedeh, Manaf Bustanji, Ahmad Aleih and Fawzi Abukhamseh
This study aims to develop a framework to incorporate Waste Cooking Oil (WCO) into asphalt mixtures. Such a framework utilizes a Balanced Mix Design (BMD) approach to ensure adequate resistance to cracking and rutting. Transportation agencies can use the...
ver más
|
|
|
|
|
|
|
|
|
|
|
Hongzhang Pan, Yongmei Zhu and Mingjiang Fang
Maraging steel is the material of deep sea pressure equipment. The characteristics of corrosion fatigue crack initiation in 18Ni (250) were investigated by performing a tensile fatigue test under different loading conditions. The mechanism of corrosion f...
ver más
|
|
|
|
|
|
|
|
|
|
|
Huayang Yu, Yihao Deng, Guansen Deng and Niya Dong
Fatigue failure in asphalt pavements, caused by continuous loading, primarily occurs at the interface between the asphalt binder and the aggregate (adhesive failure) or within the asphalt binder itself (cohesive failure). This study conducted variable st...
ver más
|
|
|
|
|
|
|
|
|
|
|
Oscar Bermejo, Juan Manuel Gallardo, Adrian Sotillo, Arnau Altuna, Roberto Alonso and Andoni Puente
Labyrinth seals are commonly used in turbomachinery in order to control leakage flows. Flutter is one of the most dangerous potential issues for them, leading to High Cycle Fatigue (HCF) life considerations or even mechanical failure. This phenomenon dep...
ver más
|
|
|
|
|
|
|
|
|
|
|
Hoang-Lan-Anh Le, Thuan-Loc Tran, Thu-Thuy Nguyen, Tran-Lan-Khue Pham and Van-Khoa Pham
The present study aims to measure the number of cycles leading to fracture (NCF) of instruments in static and dynamic cyclic fatigue situations under body temperature in stainless steel double-curved canals. The framework was constructed to establish the...
ver más
|
|
|
|
|
|
|
|
|
|
|
Wei Peng and Weijie Fan
In order to study the corrosion time-varying law and fatigue properties of high-strength steel strands used for marine environment structures, the accelerated corrosion test of steel strands was carried out by using a climate simulation chamber, and samp...
ver más
|
|
|
|
|
|
|
|
|
|
|
Huating Chen, Yifan Zhuo, Yubo Jiao and Weigang Bao
The fatigue safety of cable-girder anchorage structures in cable-stayed bridges under long-term service has attracted much attention. For bridges located in seasonally cold regions, the effect of low-temperature environments should be considered when eva...
ver más
|
|
|
|
|
|
|
|
|
|
|
Lei Li, Xianxian Zhao and Junwei Cheng
In recent years, shape memory alloys (SMAs) have been applied in the vibration control of engineering structures due to their special properties such as super elasticity and high damping, and the study of the performance of SMA wires has been relatively ...
ver más
|
|
|
|
|
|
|
|
|
|
|
Gabriela Hammes and Liseane Padilha Thives
One alternative measure to minimise the stormwater runoff volume and its pollutants and reduce impervious areas is to use permeable pavement. However, due to weak mechanical performance under heavy-load traffic related to fatigue resistance, porous mixtu...
ver más
|
|
|
|
|
|
|
|
|
|
|
Yuxuan Xia, Jingxia Yue, Jiankang Lei, Ke Yang and Yordan Garbatov
The welding residual stress re-distribution behavior during fatigue crack propagation in butt-welded high-strength steel plates for ship construction is investigated based on experimental test results and numerical analyses. The specimens? initial weldin...
ver más
|
|
|
|
|
|