Leakage Current Conduction Mechanism of Au-Pt-Ti/ HfO2-Al2O3/n-InAlAs Metal-Oxide-Semiconductor Capacitor under Reverse-Biased Condition

Resumen

Au-Pt-Ti/high-k/n-InAlAs metal-oxide-semiconductor (MOS) capacitors with HfO2-Al2O3 laminated dielectric were fabricated. We found that a Schottky emission leakage mechanism dominates the low bias conditions and Fowler?Nordheim tunneling became the main leakage mechanism at high fields with reverse biased condition. The sample with HfO2 (4 m)/Al2O3 (8 nm) laminated dielectric shows a high barrier height ?B of 1.66 eV at 30 °C which was extracted from the Schottky emission mechanism, and this can be explained by fewer In?O and As?O states on the interface, as detected by the X-ray photoelectron spectroscopy test. These effects result in HfO2 (4 m)/Al2O3 (8 nm)/n-InAlAs MOS-capacitors presenting a low leakage current density of below 1.8 × 10-7 A/cm2 from -3 to 0 V at 30 °C. It is demonstrated that the HfO2/Al2O3 laminated dielectric with a thicker Al2O3 film of 8 nm is an optimized design to be the high-k dielectric used in Au-Pt-Ti/HfO2-Al2O3/InAlAs MOS capacitor applications.