Resumen
This study explored the nitrate reduction by Al-Fe alloy. The nitrate conversions of fresh, 30-day and 90-day alloys were 78.1%, 42.8% and 9.5%, respectively. Water activation promoted the reducing ability of the alloy (98% nitrate removal), which was higher than that of copper deposited alloy (66%) and H2-reducing/acid/alkali/Cl- activated alloy (no enhancement). The effects of pre-treatments on the surface O fraction changes confirmed the activation results. With increased Fe:Al mass ratio in the alloy, nitrate conversion initially decreased and then increased again, verifying the proposed electron-donator activity of Al or Fe in alloys. Al-Fe30 had the highest NO3- conversion and Al13Fe4 content, so Al-Fe30 was selected. Significant differences in conversion were observed in alloy usages of 5?10 and 15?30 g/L. High reduction performance (nitrate below the detection limit and 19.1% N2 selectivity) was achieved under the optimal conditions: 15 g/L Al-Fe30, 150 min reaction and without pH adjustment. The rate constants of nitrate removal, nitrogen generation and ammonia generation were k1 = 1.43 × 10-2, k2 = 3.41 × 10-2 and k3 = 10.58 × 10-2 min-1, respectively. The value of (k2 + k3)/k1 was 10, indicating that the conversion of nitrate into nitrite was the rate-determining step. The repetition reaction was performed, and the rate constant decreased as the reaction step was repeated.