Resumen
Marble and limestone have been extensively used as building materials in historical monuments. Environmental, physical, chemical and biological factors contribute to stone deterioration. The rehabilitation of stone damage and the delay of further deterioration is of utmost importance. Inorganic nanoparticles having chemical and crystallographic affinity with building materials is very important for the formation of protective coatings or overlayers. In the present work, we have tested the possibility of treating calcitic materials with suspensions of amorphous calcium carbonate (am-CaCO3, ACC) and amorphous silica (AmSiO2). Pentelic marble (PM) was selected as the test material to validate the efficiency of the nanoparticle suspension treatment towards dissolution in undersaturated solutions and slightly acidic pH (6.50). Suspensions of ACC and AnSiO2 nanoparticles were prepared by spontaneous precipitation from supersaturated solutions and by tetraethyl orthosilicate (TEOS) hydrolysis, respectively. The suspensions were quite stable (nine days for ACC and months for AmSiO2). ACC and Am SiO2 particles were deposited on the surface of powdered PM. The rates of dissolution of PM were measured in solutions undersaturated with respect to calcite at a constant pH of 6.50. For specimens treated with ACC and AmSiO2 suspensions, the measured dissolution rates were significantly lower. The extent of the rate of dissolution reduction was higher for AmSiO2 particles on PM. Moreover, application of the nanoparticles on the substrate during their precipitation was most efficient method.