Resumen
The high-temperature annealing effect of a V2O5/Al2O3 bilayer on the reflectivity of visible band was studied in the present work. It was found that the V2O5 (200 nm)/Al2O3 (30 nm) sample (A-0) has a nano-granular surface morphology without a definite crystalline phase. The reflectance of A-0 overreaches 60% as the wavelength is larger than 650 nm, and its minimum reflectance (20%) occurs at the wavelength of ~500 nm. After in situ annealing treatment at 750 °C for 30 min, a triclinic AlVO4 phase appears while the nano-granular surface morphology remains (sample A-30). The reflectivity of A-30 is well suppressed in comparison with that of A-0 especially in the long wavelength range. Its minimum reflectivity approaches 5% at ~500 nm wavelength. It is speculated that the appearance of a new AlVO4 nanophase is the main reason for the decline of reflectivity. Extending the annealing time to 60 min, the reflectivity spectrum, as well as the surface morphology, are almost the same. These results can be helpful for applications of vanadium alumina nanocomposites in high-temperature environments.