Jiyoon Choi, Jiha Seong, Sangbin Park, Hyungmin Kim, Sangmo Kim, Kyung Hwan Kim and Jeongsoo Hong
Ag2O thin films have been applied in various devices, such as photodetectors, photocatalysts, and gas sensors, because of their excellent thermal stability, strong electrical properties, and stable structures. However, because various phases of silver ox...
ver más
|
|
|
|
|
|
|
|
|
|
|
Qiujin Wang, Guozhong Zhao and Hai Wang
The high-temperature annealing effect of a V2O5/Al2O3 bilayer on the reflectivity of visible band was studied in the present work. It was found that the V2O5 (200 nm)/Al2O3 (30 nm) sample (A-0) has a nano-granular surface morphology without a definite cr...
ver más
|
|
|
|
|
|
|
|
|
|
|
Carlos Ocampo-Ortega, Ines Riech, Arturo Abelenda, Ricardo Mis-Fernández, Patricia Rodríguez-Fragoso and Julio Mendoza-Alvarez
Tin sulfide (SnS) thin films were deposited by the chemical bath deposition technique. The used procedure allows us to obtain orthorhombic SnS in 3.5 h and achieve thicknesses of 390 nm. We study the influence of deposition times, percentage of Sn precur...
ver más
|
|
|
|
|
|
|
|
|
|
|
Nguyen Thai Cuong, Sophie Barrau, Malo Dufay, Nicolas Tabary, Antonio Da Costa, Anthony Ferri, Roberto Lazzaroni, Jean-Marie Raquez and Philippe Leclère
The effect of the post-annealing process on different properties of poly (L-lactic acid) (PLLA) nanofibers has been investigated in view of their use in energy-harvesting devices. Polymeric PLLA nanofibers were prepared by using electrospinning and then ...
ver más
|
|
|
|
|
|
|
|
|
|
|
Jin-Cherng Hsu and Yu-Shen Ma
In this study, we investigated the luminous properties of undoped cesium iodide (CsI) and Na-doped CsI (CsI:Na) films deposited by thermal vacuum evaporation and treated with different substrate temperatures, post-annealing temperatures, and deposition r...
ver más
|
|
|
|
|
|
|
|
|
|
|
Umut Cindemir, Pia C. Lansåker, Lars Österlund, Gunnar A. Niklasson and Claes-Göran Granqvist
Reactive dual-target DC magnetron sputtering was used to prepare In?Sn oxide thin films with a wide range of compositions. The films were subjected to annealing post-treatment at 400 °C or 500 °C for different periods of time. Compositional and structura...
ver más
|
|
|
|
|
|