The high-temperature annealing effect of a V2O5/Al2O3 bilayer on the reflectivity of visible band was studied in the present work. It was found that the V2O5 (200 nm)/Al2O3 (30 nm) sample (A-0) has a nano-granular surface morphology without a definite cr...
ver más
|
|
|
|
|
|
|
|
|
Rafal Chodun, Bartosz Wicher, Katarzyna Nowakowska-Langier, Roman Minikayev, Marlena Dypa-Uminska and Krzysztof Zdunek
This paper presents the experimental results of high-temperature sputtering of nickel targets by the Gas Injection Magnetron Sputtering (GIMS) technique. The GIMS technique is a pulsed magnetron sputtering technique that involves the generation of plasma...
ver más
|
|
|
|
|
|
|
|
|
Haixiao Fang, Hongjian Zhao and Jining He
In this study, Ti/Cu multilayer film was deposited by magnetron sputtering and then nitrided at 800 and 900 °C in N2. The microstructure and wear performance were studied. The deposited Ti/Cu multilayer film mainly consisted of Ti and Cu phases. After ni...
ver más
|
|
|
|
|
|
|
|
|
Sahand Behrangi, Ivo Sedlácek, Ján ?terba, Gabriela Suková, Zsolt Czigány, Vilma Bur?íková, Pavel Soucek, Vjaceslav Sochora, Katalin Balázsi and Petr Va?ina
Pathogenic microbes, such as bacteria and viruses, can spread quickly via contaminated surfaces. Most of these pathogenic microorganisms can survive on surfaces for a long time. Touching these surfaces can lead to the transmission of the microorganisms t...
ver más
|
|
|
|
|
|
|
|
|
Tao Wang, Yifan Wang, Qi Cheng, Shouming Yu and Guojun Zhang
CrNx coatings with a low nitrogen content below 31.7 at.% were deposited using closed field unbalanced magnetron sputtering by varying the N2:Ar flow ratio. A dense and column-free CrNx coating was obtained at a nitrogen content of 14.8 at.%, whereas the...