A niobium film on an AISI 5135 steel substrate was exposed to submillisecond pulsed electron-beam irradiation with controlled energy modulation within a pulse to increase the film?substrate adhesion. This modulated irradiation made it possible to dope the steel-surface layer with Nb through film dissolution in the layer, for which optimum irradiation conditions were chosen from experiments and a mathematical simulation. The irradiated system was tested for surface hardness and wear, and its surface structure and elemental composition were analyzed. The results demonstrate that the microhardness of the irradiated system is much higher and that its wear rate is much lower compared to the initial state.