Steel waste used in reducing emissions of nitrous oxide

Marcelo da Silva Batista    
Tássia Caroline Passos Pereira    

Resumen

 Gross wastes of the steel industry were evaluated as catalyst for the reduction of nitrous oxide. The wastes were obtained from steel mill residues (MS), lamination (LA), quenching (QC) and blast furnace powder (BF) and characterized by X-ray fluorescence (XRF), X-ray diffraction (XRD) and hydrogen temperature-programmed reduction (H2-TPR). Results revealed Si, Ca, S, Rh, Fe, Cr, Mn and Cu for all wastes, with iron featuring the greatest amount. H2-TPR analyses showed H2 consumption peaks associated with rhodium oxide, also detected by XRF. The content of comparative rhodium oxide in samples was: MS > LA > QC > BF. N2O conversion increases with increase in temperature for all catalysts. The activity of the catalysts MS > LA > QC > BF was related to rhodium oxide rate in the wastes. 

 Artículos similares

       
 
Jiamei Wu, Chenxu Zhang, Huifen Yang, Pan Chen and Jian Cao    
The development of phytoremediation technology is constrained by gentle phytoextraction efficiency and slow biomass accumulation. In this study, a combined remediation of pioneer plants and solid waste towards Cd- and As-contaminated farmland soil was ex... ver más
Revista: Applied Sciences

 
Kutalmis Recep Akça, Metin Ipek, Sevgi Çelenk, Aykut Karabulak     Pág. 87 - 101

 
Caroline Moura, Lucas Nascimento, Carlos Loureiro, Mafalda Rodrigues, Joel Oliveira and Hugo Silva    
Steel slag is a byproduct generated as waste during the steelmaking process and can be considered a cost-effective and environmentally acceptable alternative to replace natural aggregates. Using steel slag aggregates (SSA) to produce asphalt mixtures pro... ver más
Revista: Applied Sciences

 
Haibin Li, Canyang Cui, Jun Cai, Mingming Zhang and Yanping Sheng    
Steel slag (SS) is industrial waste, and there is a large amount of SS to be treated in China. Its disposal generates severe environmental pollution. One of the best ways to use SS is as a road base material. This paper reviews the possibility of using S... ver más
Revista: Coatings

 
Karel ?ramhauser, Nata?a Náprstková, Jan Sviantek, Dana Stanceková, Nguyen Van Tuong and Jan Novotný    
This article deals with the comparative wear of CNMG-coated sintered carbide indexable cutting inserts by several manufacturers when turning 1.6582 steel hardened to 40?44 HRC. The main goal will be to demonstrate the different course of wear by testing ... ver más
Revista: Coatings